Seed early strength Agent 7044 is a powdered nanocrystalline seed early strength agent based on hydrated calcium silicate, designed to promote the early hydration process of cement within 24 hours. This innovative product is widely used in high aluminum systems and sulfur aluminum systems, showing a significant effect on promoting coagulation and early strength.
One of the outstanding features of seed early strength agent 7044 is its strong adaptability. Whether under low temperature or hot curing conditions, it can effectively promote the hardening of cement, especially under low temperature conditions. This enables the 7044 to perform well in a wide range of environmental conditions.
In addition, seed early strength agent 7044 also has excellent compatibility for a variety of cement systems such as ordinary Portland cement, sulphoaluminate cement and high aluminate cement. Its incorporation can not only accelerate the setting of cement, but also significantly improve the early strength, so that the construction progress of the project can be greatly improved.
In the field of application, seed early strength agent 7044 is widely used in high performance mortar such as sulfur aluminum system mortar, high aluminum system mortar repair mortar, grouting material, self-leveling, tile glue and so on. The recommended dosage is 0.1% to 1.0% of the quality of the rubber material to achieve the best performance improvement effect.
Comparative test:
Water binder ratio 0.5
Test number Test 1 Test 2 Test 3
Blank early strength agent 7044 lithium carbonate
Double fast aluminum cement double fast aluminum cement double fast aluminum cement
Standard sand Standard sand standard sand
2 hours intensity 10℃ curing 10℃ curing 10℃ curing
No hardening three tests Three tests
Average 5.4 mpa average 3.4 mpa
24-hour intensity
10℃ Curing 10℃ curing
Three sets of tests Three sets of tests
14.4 mpa 7.7 mpa
It is worth noting that compared with traditional lithium carbonate, seed early strength agent 7044 performs better in terms of strength enhancement, and the late shrinkage is almost negligible. This advantage makes the 7044 more advantageous in engineering projects, providing engineers and architects with greater design and construction flexibility.
Overall, seed early strength Agent 7044, with its innovative technology and wide range of applications, is bringing breakthrough changes to the cement-based materials industry. Its excellent early strength enhancement, strong adaptability and wide compatibility make it an integral part of today's engineering projects.